透光范圍

420-5200nm

120-8500nm

200-2300nm

晶體結(jié)構(gòu)

Trigonal,SpaceGroup R3c

Trigonal,SpaceGroup R3c

Trigonal,SpaceGroup R3c

晶系

Positive Uniaxial

Positive Uniaxial

Negative Uniaxial

含晶細(xì)胞

a=b=0.515 ?,c=13.863 ?

a=b=4.621 ?,c=3.053 ?

密度

4.64g/cm3

3.18g/cm3

2.65g/cm3

潮解性

Low

Low

Low

莫氏硬度

5

6

7

熱膨脹系數(shù)

Aa=2.0*10﹣6/k@25℃

Ac=2.2*10﹣6/k@25℃

Aa=6.23-9.25*10﹣6/k

Ac=10.86-14.54*10﹣6/k

Aa=6.2*10﹣6/k

Ac=10.7*10﹣6/k

光學(xué)均勻性

5*10﹣5/cm

10﹣6/cm

10﹣6/cm

吸收系數(shù)

0.1%/cm﹣1@1064nm

0.07at 0.2um;0.02 at 5.0um

0.02@500nm

0.1%/cm﹣1@1064nm

在45°時(shí)屈光指數(shù)，雙折射，離散角（ρ）

Ne=2.20263,No=2.28629

△   n=0.08366

ρ=2.135°@633nm

Ne=1.38876,No=1.37698

△   n=0.01178

ρ=0.488°@633nm

Ne=1.55170,No=1.54265

△   n=0.00905

ρ=0.335°@532nm

直徑

Max.30-40mm

Max.50mm

Max.100mm

長(zhǎng)度

Max.25-35mm

Max.100mm

Max.100mm

光潔度

Better than 20/10 Scratch/Dig Per MIL-0-13830A

光束偏離

<10arc seconds

光軸方向

+/-0.2°

面形

<λ/8@633nm

透過(guò)波前畸變

<λ/4@633nm

鍍膜

Upon Specification